Terry,
You really made me laugh with your answer!!
I pictured myself with the electrodes and wires inside my mouth! I am sure
stirring with my tongue would be quite simple...!
Thank you again for helping me learn.
Take care
From: Terry Chamberlin tcj...@yahoo.ca
Reply-To: silver-list@eskimo.com
To: silver-list@eskimo.com
Subject: CSSilver wire, etc.
Date: Fri, 15 Sep 2006 07:24:36 -0400 (EDT)
Carlos said,
I am getting a bright, slightly darkened plating
on the inside of the 450 ml glass I use to produce my
CS. Could this also happen to my teeth?
Yes, if you were making CS in your mouth.
Is .999 silver good enough to make new electrodes? It
is the best I have found here so far to make larger
diameter electrodes. The ones this generator brought
are 0.8 mm wire. Too thin in my opinion.
.999 is perfectly fine. There is absolutely NO
evidence that CS made with . (or .9) is better
or more effective or safer than .999 silver.
Every silver wire, however thick it is to start, will
eventually become as thin a a hair, as it is
dissolving into water as you are making CS.
Eventually, when you make as much CS as I make (20-30
gallons per week), you end up with a bunch of little
silver wire ends. I just twist them around each other
and use them as an electrode. Waste not!
Terry Chamberlin
__
Do You Yahoo!?
Tired of spam? Yahoo! Mail has the best spam protection around
http://mail.yahoo.com
--
The Silver List is a moderated forum for discussing Colloidal Silver.
Instructions for unsubscribing are posted at: http://silverlist.org
To post, address your message to: silver-list@eskimo.com
Address Off-Topic messages to: silver-off-topic-l...@eskimo.com
The Silver List and Off Topic List archives are currently down...
List maintainer: Mike Devour mdev...@eskimo.com
_
FREE pop-up blocking with the new MSN Toolbar - get it now!
http://toolbar.msn.click-url.com/go/onm00200415ave/direct/01/