From: [EMAIL PROTECTED]
To Steve ET
It is more than just thought it is knowledge (see below)
the thought given by Walter ([EMAIL PROTECTED]) was that
the indented area would be especially subject to being
the weakest point. Might I suggest a method I use to
reclaim the copper and brass
From: "E.J. Totty", [EMAIL PROTECTED]
NO WAY WOULD I ANNEAL USED PRIMERS, YOUR APPLICATION THE USE THEREOF
IS OK, BUT REMEMBER PRIMERS ARE SUBJECT TO CONSIDERABLY MORE PRESSURE.
IF YOU'VE EVER SEEN SOFT BRASS FLOW UNDER PRESSURE, YOU WON'T DO IT
TWICE.
PRIMER CUPS NEED TO HAVE A CERTAIN