Hi all
I have a complex oxide BaTi8-xGaxO16. What standards I should run?
Ga is the dopant. I guess I should run the sample without dopant BaTi8O16
as standard, or the simple oxide as BaO, TiO2 Ga2O3? or is the standard
necessary?
Also, I have colleage working on DFT, I assume the theoretical
You didn't say what you're trying to find out or even which edge you're doing
this at. That being the case, it's a little hard to know
what the best strategy is. A few things come to mind:
1. If you're looking for the environment of the Ga, then obviously, BaO
and Ti2O3 aren't terribly
...@millenia.cars.aps.anl.gov] on behalf of Matthew Marcus
[mamar...@lbl.gov]
Sent: Tuesday, November 18, 2014 6:09 PM
To: XAFS Analysis using Ifeffit
Subject: Re: [Ifeffit] experimental standard
You didn't say what you're trying to find out or even which edge you're doing
this at. That being the case, it's a little
, 2014 6:09 PM
To: XAFS Analysis using Ifeffit
Subject: Re: [Ifeffit] experimental standard
You didn't say what you're trying to find out or even which edge you're doing
this at. That being the case, it's a little hard to know
what the best strategy is. A few things come to mind:
1