Hi, Fracois,
Take a look in the book "Powder diffraction, Theory and practice" edited
by Dinnebier and Billinge, published by The Royal Society of Chemistry,
2008. In chapter 12, page 347 you can find the texture strength for
spherical harmonics - formula (52). You have only to add a factor 1/4
Dear Rietveld users,
I am currently testing the Spherical Harmonic Preferential Orientation
(SH-OP) correction implemented in the last version of HighScorePlus.
It is working nicely, nevertheless I would like to compare the old
March-Dollase correction parameter with the new SH-OP parameters
Dear Christian (and others)
your reply about preferred orientation probabaly not being a problem with a cubic
mineral is of interest to me.
This is something I have wondered about in the past because of observations I have
made on common salt, so I thought I would contribute to this discussion
Dear Stephen,
You are quite correct. I was going to make the same reply to Christian's
comment also using NaCl as an example. What I would add though is that NaCl
may be more prone to preferred orientation as the cubes are close to
perfect - in contrast to say cubic zeolites where I have
your reply about preferred orientation probabaly not being a problem with
a cubic mineral is of interest to me.
I can testify to have seen huge preferred orientation occuring
in some cubic perovskites, at least. Too much intensity in those
h00.
Armel
Could you please advise me how must prepare my powder to obtain a pattern=
without preferentiel orientation.
My sample is a zeolite X exchanged
I'm going to do a strucutre resoltion and its affinmey using the Rietveld=
commercial software
With many thanks for your help and best regards,
Dear Ouassyla
since zeolite X is cubic I do not think that you will have any problems with preferred orientation! Just sit back, relax and enjoy the beautiful structure ;-)
Best
Christian Baerlocher
On May 30, 2004, at 9:38 PM, fatiha belarbi wrote:
Dear All,
Could you please advise me how
n.
I hope it will help.
With best regards,
Husin
-Original Message-From: fatiha belarbi
[mailto:[EMAIL PROTECTED] Sent: Sunday, May 30, 2004 1:39
PMTo: [EMAIL PROTECTED]Subject: preferential
orientation
Dear All,Could you please advise me how must prepare my powder to
obtain