It appears that the right-hand column did not post correctly; so I am reposting the part that includes the right-hand column and hope that it comes through okay.
In a message dated 98-02-21 12:36:44 EST, [email protected] writes: << Following are the results of colloidal silver solution preparation made on January 26, 1998: SAMPLE SAMPLE SAMPLE A2X B1Y C3Z 1. ounces of boiled,distilled water: 8 6 6 2. ounces of starter solution: 8 2 2 3. duration of process (minutes): 18 10 11 4. ambient (room) temp in degrees Fahrenheit: 77 77 77 5. weather: sunny sunny sunny 6. electrode separation (inches): 3/8 1/2 3/8 7. temperature in degrees Fahrenheit of water that bottle is placed in: 170 170 172 8. approx. time of day (p.m.) 2:30 3:00 3:30 9. number of times electrodes cleaned: 3 1 2 10. color of final solution: golden, golden, golden light medium medium 11. ppm as measured by Aqualab, Tucson, AZ: 25 34 36 Notes: a. Sample A2X was the starter solution. b. The lower half of the bottle containing the colloidal silver solution was placed in a pan of heated water. The water was heated over a natural gas burner. c. The electrodes (99.99% pure) used were those supplied by Action Electronics. d. The electrodes were approxately 90% covered by the colloidal silver solution. e. Electrode separation was measured at the end of the electrodes. The electrode separation at the beginning was about 1/8 inches. Hope that the above information helps in our research. >>
--- Begin Message ---Following are the results of colloidal silver solution preparation made on January 26, 1998: SAMPLE SAMPLE SAMPLE A2X B1Y C3Z 1. ounces of boiled,distilled water: 8 6 6 2. ounces of starter solution: 8 2 2 3. duration of process (minutes): 18 10 11 4. ambient (room) temp in degrees Fahrenheit: 77 77 77 5. weather: sunny sunny sunny 6. electrode separation (inches): 3/8 1/2 3/8 7. temperature in degrees Fahrenheit of water that bottle is placed in: 170 170 172 8. approx. time of day (p.m.) 2:30 3:00 3:30 9. number of times electrodes cleaned: 3 1 2 10. color of final solution: golden, golden, golden, light medium medium 11. ppm as measured by Aqualab, Tucson, AZ: 25 34 36 Notes: a. Sample A2X was the starter solution. b. The lower half of the bottle containing the colloidal silver solution was placed in a pan of heated water. The water was heated over a natural gas burner. c. The electrodes (99.99% pure) used were those supplied by Action Electronics. d. The electrodes were approxately 90% covered by the colloidal silver solution. e. Electrode separation was measured at the end of the electrodes. The electrode separation at the beginning was about 1/8 inches. Hope that the above information helps in our research. Harry Davis -- The silver-list is a moderated forum for discussion of colloidal silver. To join or quit silver-list or silver-digest send an e-mail message to: [email protected] -or- [email protected] with the word subscribe or unsubscribe in the subject: line. To post, address your message to: [email protected] List maintainer: Mike Devour <[email protected]>
--- End Message ---