Hi All you Responders;
I will try to answer all of the questions on this go around. Both brew
conditions the same except for arc electrode point not resharpened
between brews.
The DW was from Wal-Mart, Conductivity = 0 to 1 uS
DW quantity 2 liters in a 4 1/2" cylinder 11" tall. about 2" of free
board above water surface.
Total wet surface 2" x 5-1/2" x .04" in several pieces.
Voltage 12 kv sign transformer
Brew time = 3 hours
Definate ozone smell during and after brew.
Lot #6022A Date 6/02/00
PPM = 15.4 ; Cond. =870 uS ; Temp at end of brew 90 deg. F.;
T.E. very weak; Iac = 25.8 ma +/- .2 ma; no metallic taste slight
acidic
Lot #6032A Date 6/03/00
PPM = 17.6; Cond. = 1125 uS; Temp at end of brew 97 deg. F.;
T.E. medium; Iac =24 ma +/- .2 ma; no metal taste but acidic
Continuos mechanical stirring. This makes the T.E. uniform top to bottom
during brew, rather than graded from strong to very weak at the bottom.
There is one variable not accounted for and that is arc length. In both
cases the arc was blue with a plasma around it, and there was tip melt
back.
"Ole Bob"