Re: CS>high ppm CS experiment, was Re: CS>CS site From: sol Date: Wed, 23 Mar 2005 19:44:13 http://escribe.com/health/thesilverlist/m78777.html
> Mike, > I have in previous years run a couple of other high ppm batches > (all were pints, as the one below was), but don't have records on > those. > It does seem to me that going above 15 or 20 ppm introduces a lot > more variables into the process, or perhaps it is just inherently > more susceptible to minute variables or water or air contaminants > with larger batch sizes. The particular batch below is the only > one of about 3 high ppm batches I've made that turned out clear. > What do you mean by "poison the electrodes" ? > I will be doing some more batches of high ppm, and will try to > keep better notes. I am writing to David too. And can post results > either to the list or privately. > sol Thanks very much for your help, sol. Yes, I found getting to 20uS is reasonably easy, then it seems to hit a brick wall. Every increment in performance becomes twice as difficult. The water has a lot to do with it, but I have no idea what it could be. I was sure David's results with demineralized water would prove to be in error, but he easily passed every test I could throw at him. His PWT reading of 53uS was astounding to me. Also note he uses magnetic stirring, and I believe you have thermal. This shows the high PWT readings are possible under very different conditions, so the process may turn out to be quite robust. Some time ago, I reported an extremely hard and very black coating on the electrodes that would not come off even when I tried scraping. The WalMart dw suddenly changed, and the cs started behaving very strange. This was an attempt to kill mold spores in my blankets, and I was adding H2O2 to convert any oxides to ions to gain a bit more strength. When I added the H2O2, the 4 litre jar instantly turned brilliant yellow, then white. It was like a miniature atomic explosion. It took a lot of H2O2 to turn the solution clear again. After I found better dw, I noticed the hard coating on the cathode starting to disappear. It took 7 or 8 brews, swapping the electrodes each time, to finally remove the coating. That's what I meant by "poisoning" the electrodes. The topic of high uS may be of great help to others. I made my first batch of 44.9uS cs on March 4. Three weeks later, on March 20, about half the symptoms from mold toxins have disappeared. I was taking 20uS cs for years with no effect, but increasing the strength has really made a difference. My new cs generator works, but it uses fairly high voltage that could be lethal, and would be difficult for many people to duplicate. It would be wonderful to find a simpler process that anyone could use, and even better if it utilized a readily available and well known product. Please post results to the list so all those who may be interested can view them. Best Wishes, Mike Monett -- The Silver List is a moderated forum for discussing Colloidal Silver. Instructions for unsubscribing are posted at: http://silverlist.org To post, address your message to: [email protected] Silver List archive: http://escribe.com/health/thesilverlist/index.html Address Off-Topic messages to: [email protected] OT Archive: http://escribe.com/health/silverofftopiclist/index.html List maintainer: Mike Devour <[email protected]>
