At 05:26 PM 8/13/2008 -0500, you wrote:
Carrole,
Simple answer, if one of your rods turns black, you are making colloidal
silver. How much and how fast is something else. The black is silver oxide
forming on the negative electrode. The faster the black forms the faster
you are generating colloidal silver. If one rod does not turn black, you
are not creating colloidal silver or you are doing so at a very slow rate.
A number of factors affect the rate at which you generate colloidal
silver. The primary ones are the voltage across the rods, the spacing
between the rods and the amount of colloidal silver (or impurities) in the
water. The more colloidal silver in the water, the faster you generate
additional colloidal silver. Because of this I add some colloidal silver
to the distilled water to speed up the process. Some people add sea salt
to do the same thing but I do not recommend that. You could add salt to a
test sample to determine whether your generator is working (ie turning one
rod black) and then discard the test solution after the test.
If you started with pure distilled water and no colloidal silver added to
it, it can take a very long time to start generating colloidal silver. You
can under this condition, move the rods closer together, about 1 and 1/2
inches apart. That will significantly speed up generating colloidal silver
but will generate a little larger silver colloids. I have done this to get
the procsess started and then moved the rods farther apart (2 and 1/2
inches) after things are going well. Then I save 1 or 2 ounces of
colloidal silver to add to the next batch I make as a starter.
I hope this helps.
- Steve
----------
From: Carrole Orme [mailto:captain_sun...@yahoo.ca]
Sent: Wednesday, August 13, 2008 1:54 PM
To: silver-list@eskimo.com
Subject: CS>Silver rods
Hi
I tried the light through the container and got a faint beam
I am wondering if my silver rods are not putting out much silver
Could this be possible?
I want to know what might be wrong with not getting as much CS
in my containers
In the beginning I seen particules and when I wiped the silver rods off
there was black stuff
Now I get hardly nothing
I would like stronger CS
Could anyone help me figure out what is going on with my CS and be able to
make stronger CS?
Thanks Carrole
<http://ca.toolbar.yahoo.com/>Yahoo! Canada Toolbar
:<http://ca.toolbar.yahoo.com/> Search from anywhere on the web and
bookmark your favourite sites. Download it now!
No virus found in this incoming message.
Checked by AVG - http://www.avg.com
Version: 8.0.138 / Virus Database: 270.6.3/1611 - Release Date: 8/14/2008
6:20 AM
--
The Silver List is a moderated forum for discussing Colloidal Silver.
Instructions for unsubscribing are posted at: http://silverlist.org
To post, address your message to: silver-list@eskimo.com
Address Off-Topic messages to: silver-off-topic-l...@eskimo.com
The Silver List and Off Topic List archives are currently down...
List maintainer: Mike Devour <mdev...@eskimo.com>