I recommend you stay with your 1.4 mA current limiting diode. Just let it
run longer, e.g. 24 hours is convenient. Lower current will make finer
particles, and reduces the need for stirring. If you need to make CS
faster, then use a quart container instead of a half-gallon.
--Steve Y.
Keith,
See Wayne's comment below. I suspect with your 30 volt supply (which is
probably higher with only a 1.4 mA load), you probably start drawing 1.4 mA
the moment you turn it on or shortly thereafter. You would need very, very
pure water for the starting current to be lower. You shouldn't
Morning Keith,
>> If I don't use any thing to limit the milliamps the power supply
>> will put out 16 milliamps which I think is to high to use.
Do you test / check your water in any way?
It appears your electrode spacing is 2.5 to 2.625 inches or thereabout.
I still find it hard to believe t
Hi..I am using air to stir my CS and am using the TDS-3 TDS/TEMP meter to
measure the PPM. It seem that the slower the air flow into the water is the
quicker the PPM goes up. I don't really know why it wouldn't be setup right? I
have used others' diagrams and pictures but on this batch I was u
The Faraday calculator shows that 1.4 ma in 1000 ml water
for 900 minutes should result in a brew of 84.52 ppm, that
is if there were no losses and all the silver went into the
water.
You must either have a problem with your setup and it is not
working properly, or you must have a tremendous
Hi..
Someone asked me what herbs I used for my dental problem along with the CS.
I am a student of Master Herbalist, and I have purchased the herbs from the
Herb Connection. I hope I am allowed to say this.
I had a root canal gone bad, and was told I needed immediate surgery if the
symptoms
If it were me, I'd simply incorporate bentonite clay/activated
charcoal slurries into my detox program and take even MORE of
whatever was causing the herx...
Do you have a source to recommend for bentoniteclay?
The best source of information (and they do list sources for the clay) is:
http
They NOW have the power thanks to the new legislation.
Most 'legislation' is territorial in nature - ie, it only applies to
areas where Congress has what is called 'exclusive legislative
jurisdiction'. This includes Washington DC, property within any State
where jurisdiction has been offici
Evening Chuck,
You are using the easiest method devised.
You could over simplify, if you tried.
Maybe the best, not sure it is the easiest. Maybe the most foolproof also.
>> You are at a perfect place with 1.4 ma.
Your CS will be of high quality which you will spoil by raising the
curre
Evening Keith,
>>At 12:46 PM 7/21/2007, you wrote:
and have been brewing a 32ounce batch and after about 15 hours it is only
up to 7PPM
You could use 4 to 8 ounces of CS from a previous batch to help get the
batch started and up to speed.
Even one to 2 drops of saline solution would work
I wanted to know if you had an opinion on this subject. Lots of folks get
herxing reactions when using medications ie, herbs ,antibiotics etc. when
treating lyme or candida. Would you advise using this same method of charcol
and clay for help with detox? It sounds like it would be very helpful f
Keith,
You are at a perfect place with 1.4 ma.
Your CS will be of high quality which you will spoil by raising the
current.
Yes, it takes a long time. That's what it takes with LVDC systems.
There are other methods such as HVDC involving thousands of volts.
They are not simple, and can be dangerou
Hi All..Still playing around. I was wondering what the proper milliamps would
be to make the Colloidal Silver. I am using the 30vdc power supply with a
current limiting diode and my milliamps are at 1.4 mA and have been brewing a
32ounce batch and after about 15 hours it is only up to 7PPM so I
That is the same machine I have. It works pretty good, if it is in a
sufficiently small space. I even got the mold toxins out of the crawl
space under the tub with it- I admit, that is a pretty small space, but
I gave it 2 hours, and *presto* like magic I could put my hands in
there and fix t
About 6 - 10 drops of 3% H2O2 per quart of CS is usually enough and
doesn't change the flavor.
Ode
At 08:23 PM 7/20/2007 -0500, you wrote:
Evening Sol.
>>So far as I know peroxide doesn't "harm" CS, it does clear it up, but
it also makes it taste pretty nasty.
Taste a little DMSO.
Make that a couple or three DAYS after.
Add it too soon and you'll know it.
Ode
At 01:30 PM 7/20/2007 -0500, you wrote:
Add H2O2 only *after* making the CS, not before...
No one has done comparison testing of CS and CS with this small amount
of H2O2 added to test it's efficacy, but anecd
Peroxide scavenges the O out of AgO, [silver oxide..that gold stuff, or
brown to black if thick on an electrode] releasing metallic silver.
Ode
At 12:54 PM 7/20/2007 -0500, you wrote:
as I recall, something about the peroxide seems to break up the larger
colloids that cause the gold colo